METHOD OF IGZO AND ZNO TFT FABRICATION WITH PECVD SiO2 PASSIVATION

ABSTRACT

The present invention generally relates to a method of manufacturing a TFT. The TFT has an active channel that comprises IGZO or zinc oxide. After the source and drain electrodes are formed, but before the passivation layers or etch stop layers are deposited thereover, the active channel is exposed to an N 2 O or O 2  plasma. The interface between the active channel and the passivation layers or etch stop layers are either altered or damaged during formation of the source and drain electrodes. The N 2 O or O 2  plasma alters and repairs the interface between the active channel and the passivation or etch stop layers.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims benefit of U.S. Provisional Patent Application Ser. No. 61/503,413 (APPM/16107L), filed Jun. 30, 2011, which is herein incorporated by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

Embodiments of the present invention generally relate to a method of manufacturing a thin film transistor (TFT).

2. Description of the Related Art

TFTs are used as switching and driving devices in almost all integrated circuits (IC). Additionally, TFTs are utilized in the flat panel display (FPD) industry to control pixels. For many years, the primary material for TFT fabrication has been silicon. Silicon may be used for the active layer within the TFT and may be doped as desired to make the TFT function accordingly. Silicon does have its limitations. For one, silicon is not transparent. More and more companies are striving to develop transparent TFTs.

One of the materials thought to be beneficial for transparent TFTs is indium-gallium-zinc oxide (IGZO). Another material thought to be beneficial for transparent TFTs is zinc oxide. There is a need in the art for a method to fabricate TFTs utilizing IGZO and/or zinc oxide.

SUMMARY OF THE INVENTION

The present invention generally relates to a method of manufacturing a TFT. The TFT has an active channel that comprises IGZO or zinc oxide. After the source and drain electrodes are formed, but before the passivation layers or etch stop layers are deposited thereover, the active channel is exposed to an N₂O or O₂ plasma. The interface between the active channel and the passivation layers or etch stop layers are either altered or damaged during formation of the source and drain electrodes. The N₂O or O₂ plasma alters and repairs the interface between the active channel and the passivation or etch stop layers.

In one embodiment, a method comprises forming an active channel in a thin film transistor by defining source and drain electrodes, exposing the active channel to a N₂O or O₂ plasma and depositing one or more passivation or etch stop layers over the N₂O or O₂ plasma treated active channel.

In another embodiment, a method comprises forming a gate electrode over a substrate, depositing a gate dielectric layer over the gate electrode and the substrate, depositing an IGZO active layer over the gate dielectric layer, depositing a conductive layer over the active layer, removing at least a portion of the conductive layer to form source and drain electrodes and to form an active channel by exposing a portion of the active layer, exposing the active channel to a N₂O or O₂ plasma and depositing one or more passivation or etch stop layers over the N₂O or O₂ plasma exposed active channel.

In another embodiment, a method comprises forming a gate electrode over a substrate, depositing a gate dielectric layer over the gate electrode and the substrate, depositing a zinc oxide active layer over the gate dielectric layer, depositing a conductive layer over the active layer, removing at least a portion of the conductive layer to form source and drain electrodes and to form an active channel by exposing a portion of the active layer, exposing the active channel to a N₂O or O₂ plasma and depositing one or more passivation or etch stop layers over the N₂O or O₂ plasma exposed active channel.

In another embodiment, a thin film transistor includes a gate electrode disposed over a substrate, a gate dielectric layer disposed over the gate electrode and the substrate, a plasma treated active layer comprising zinc oxide or indium-gallium-zinc-oxide disposed over the gate dielectric layer, a source electrode and a drain electrode spaced apart and formed over the plasma treated active layer such that a portion of the plasma treated active layer remains exposed and one or more or etch stop passivation layers disposed over the exposed active plasma treated active layer.

BRIEF DESCRIPTION OF THE DRAWINGS

So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

FIGS. 1-9 are schematic illustrations of a TFT at various stages of fabrication according to one embodiment.

FIGS. 10A-10C show the effects of N₂O plasma treatment on the TFT.

FIG. 11 is a cross sectional view of a PECVD apparatus according to one embodiment of the invention.

To facilitate understanding, identical reference numerals have been used, where possible, to designate identical elements that are common to the figures. It is contemplated that elements disclosed in one embodiment may be beneficially utilized on other embodiments without specific recitation.

DETAILED DESCRIPTION

The present invention generally relates to a method of manufacturing a TFT. The TFT has an active channel that comprises IGZO or zinc oxide. After the source and drain electrodes are formed, but before the passivation layers or etch stop layers are deposited thereover, the active channel is exposed to an N₂O or O₂ plasma. The interface between the active channel and the passivation layers or etch stop layers are either altered or damaged during formation of the source and drain electrodes. The N₂O or O₂ plasma alters and repairs the interface between the active channel and the passivation or etch stop layers.

FIGS. 1-9 are schematic illustrations of a TFT at various stages of fabrication according to one embodiment. As shown in FIG. 1, the TFT is fabricated by depositing a conductive layer 104 over a substrate 102. Suitable materials that may be utilized for the substrate 102 include glass, soda lime glass, plastic, and semiconductor wafers. If soda lime glass is utilized as the substrate 102, one or more barrier layers will be deposited over the substrate 102 prior to depositing the conductive layer 104. Suitable materials that may be utilized for the conductive layer 104 include chromium, molybdenum, copper, aluminum, tungsten, titanium, and combinations thereof. The conductive layer 104 may be formed by physical vapor deposition (PVD) or other suitable deposition methods, such as electroplating, electroless plating or chemical vapor deposition (CVD).

As shown in FIG. 2, the conductive layer 104 is patterned to form a gate electrode 202. The patterning may occur by forming either a photolithographic mask or a hard mask over the conductive layer 104 and exposing the conductive layer 104 to an etchant. Depending upon the material utilized for the conductive layer 104, the conductive layer 104 may be patterned using a wet etchant or by exposing the conductive layer 104 not covered by the mask to an etching plasma. In one embodiment, the conductive layer 104 may be patterned by etching areas of the conductive layer 104 that are not covered by a mask with an etching plasma comprising etchants such as SF₆, O₂, Cl₂, and combinations thereof.

As shown in FIG. 3, after the gate electrode 202 has been formed, a gate dielectric layer 302 is deposited thereover. Suitable materials that may be utilized for the gate dielectric layer 302 include silicon nitride, silicon oxide, and silicon oxynitride. Additionally, while shown as a single layer, it is contemplated that the gate dielectric layer 302 may comprise multiple layers, each of which may comprise a different chemical composition. Suitable methods for depositing the gate dielectric layer 302 include conformal deposition methods such as plasma enhanced chemical vapor deposition (PECVD), CVD and atomic layer deposition (ALD).

As shown in FIG. 4, a high mobility active layer 402 is deposited. Suitable materials that may be used for the high mobility active layer 402 include IGZO and zinc oxide. The active layer 402 may be deposited by suitable deposition methods such as PVD. In one embodiment, the PVD may comprise applying a DC bias to a rotary cathode.

As shown in FIG. 5, a conductive layer 502 may be deposited over the active layer 402. Suitable materials that may be utilized for the conductive layer 502 include chromium, molybdenum, copper, aluminum, tungsten, titanium, and combinations thereof. The conductive layer 502 may be formed by PVD or other suitable deposition methods such as electroplating, electroless plating or CVD.

As shown in FIG. 6, the conductive layer 502 is patterned to form a source electrode 602 and a drain electrode 604 by a back channel etch process. The patterning may occur by forming either a photolithographic mask or a hard mask over the conductive layer 502 and exposing the conductive layer 502 to an etchant. Depending upon the material utilized for the conductive layer 520, the conductive layer 502 may be patterned using a wet etchant or by exposing the conductive layer 502 not covered by the mask to an etching plasma. In one embodiment, the conductive layer 502 may be patterned by etching areas of the conductive layer 502 that are not covered by a mask with an etching plasma comprising etchants such as SF₆, O₂, and combinations thereof. In forming the source electrode 602 and the drain electrode 604, a portion 608 of the active layer 402 is exposed. The exposed portion 608 is between the source and drain electrodes 602, 604. The area between the source and drain electrode 602, 604 is referred to as the active channel 606. As will be discussed below, one or more passivation layers will be formed over the active channel 606.

Due to the high sensitivity of IGZO TFTs at the interface of IGZO, more specifically at the active channel 606, and passivation layers (PV), an etch stop layer has been adapted for TFT fabrication to prevent channel damage during etching of the conductive layer 502. However, the etch stop layer fabrication requires more mask steps and significantly increase the manufacturing cost. In the etch stop device manufacturing process, the etch stop layer is deposited prior to deposition of the conductive layer that is patterned/etched to define the source and drain electrodes.

Alternatively, the back channel etch process described above utilizes fewer masks than the etch stop layer fabrication process and has a simple process flow for low cost fabrication of IGZO TFTs. However, preventing interface damage and charge accumulation at the IGZO-PV interface during source-drain formation by etch process is a challenge. Therefore, an N₂O or O₂ plasma treatment is performed directly after the source-drain etch and before the passivation layer deposition. Without this plasma pre-treatment, IGZO TFTs will either fail to show any TFT characteristics or perform poorly under thermal bias stress. As shown in FIG. 7, the partially fabricated TFT is exposed to a N₂O or O₂ plasma 702. The N₂O or O₂ plasma 702 is formed in-situ the chamber in which the conductive layer 502 was patterned. The plasma treatment can occur prior to forming the etch stop layers (for an etch stop layer device) or before depositing the passivation layers (for a back channel etch device).

It has surprisingly been found that N₂O or O₂ plasma is the most effective plasma to utilize to ensure a consistent TFT is fabricated. Plasma formed from argon or N₂ is too mild to have a significant effect on the active channel. It should also be noted that the N₂O or O₂ plasma treatment will not be effective for silicon based TFTs. The oxygen from the N₂O or O₂ plasma will react with the silicon in the active channel to form silicon oxide and cause the TFT to fail.

The passivation layer is the topmost layer of TFT devices which protects the devices from environment damage, including chemical or mechanical effects. The passivation layer also provides stable and reliable TFT performance against prolonged thermal and electrical bias stress. Due to the sensitivity of active materials, such as IGZO and zinc oxide, toward hydrogen and other environmental chemicals, high quality low hydrogen contain oxides, such as TiO₂ and silicon oxides, are preferred for the passivation layer instead of conventional silicon nitride (SiN_(x)).

As shown in FIGS. 8 and 9, multiple passivation layers 802, 902 are deposited over the active channel 606 and the source and drain electrodes 602, 604. The first passivation layer 802 that is in contact with the exposed portion 608 of the active layer 402 comprises a low hydrogen containing oxide. The second passivation layer 902 is formed over the first passivation layer 802 and can comprise one or more additional layers of low hydrogen containing oxide, silicon nitride, silicon oxynitride, or combinations thereof.

When silicon oxide is used as the first passivation layer 802, the silicon oxide can be deposited either by PVD or PECVD. Considering the plasma damage associated with PVD, PECVD is the state of art approach to deposit a SiO₂ passivation layer because of highly conformal deposition results and less plasma damage to the deposited films. PECVD silicon oxide is normally performed with TEOS+O₂ or SiH₄+N₂O as the source gases, where the former provides better film quality than the latter. TEOS-based silicon oxide PECVD processes are difficult to scale up, particularly to process substrates that have a surface area of 43,000 cm² and above. However, the SiH₄-based silicon oxide PECVD process can be scaled up to process substrates that have a surface area of 43,000 cm² and above. The N₂O or O₂ plasma treatment on the active layer prior to the deposition of the first passivation layer 802 has shown to enable the TEOS-based silicon oxide PECVD process to scale up to substrates that have a surface area than 43,000 cm² and above. Once the first and second passivation layers 802, 902 have been deposited, the TFT 900 is complete.

In general, the N₂O or O₂ plasma treatment may occur at a chamber pressure of between about 0.8 Torr and about 2.5 Torr. The RF power applied to the electrode to ignite and maintain the plasma may be between about 0.083 watts/cm² to about 1.0 watt/cm². The substrate may be maintained at a temperature of between about 150 degrees Celsius and about 270 degrees Celsius during the plasma treatment. The substrate may be spaced from the electrode by a distance of between about 500 mils to about 1100 mils. For N₂O plasma treatment specifically, the pressure may be between about 0.8 Torr and about 1.2 Torr while the spacing is maintained between about 500 mils and about 800 mils to maintain a uniform distribution of the plasma.

TABLE Step 1 2 3 4 5 6 7 Time (sec) 120 30 30 15 158 15 97 Process power set 0 0 600 0 715 0 600 point Process spacing 500 500 500 500 500 800 800 (mil) Process pressure 800 12000 1200 800 800 1200 1200 (mtorr) N₂O 5658 5658 5658 5658 5658 0 0 N₂ 0 0 0 0 0 3500 3500 NH₃ 0 0 0 0 0 600 600 SiH₄ 0 0 0 48 48 60 60

The table above shows the processing conditions according to one embodiment for not only the N₂O plasma treatment, but also for forming a first and second passivation layer. Each of the steps that occur in the table above occur in-situ the same processing chamber, such as a PECVD processing chamber available from AKT, a subsidiary of Applied Materials, Inc., Santa Clara, Calif. It is to be understood that the process may be performed in other chambers, including those sold by other manufacturers. The processing conditions identified in the table above occurred in a processing chamber sized to process a substrate having a surface area of about 2,000 cm².

In step 1, N₂O is introduced to the processing chamber at a flow rate of about 5658 sccm while the substrate is spaced about 500 mils from the gas distribution showerhead. The processing chamber pressure is maintained at about 800 mTorr for about 120 seconds. No other gases are introduced to the processing chamber during step 1. Then, in step 2, while maintaining the substrate to gas distribution showerhead spacing at about 500 mils, the chamber pressure is increased to about 1200 mTorr for over a time period of about 30 seconds. During step 2, no additional gases are introduced into the processing chamber, and the N₂O gas in the processing chamber ignited into a plasma. The N₂O gas in step 2 continues to be introduced at a flow rate of about 5658 sccm. In step 3, the processing chamber has reached the pressure of about 1200 mTorr. The substrate to gas distribution showerhead spacing remains about 500 mils and the N₂O gas flow rate remains at about 5658 sccm. For a time period of about 30 seconds, an RF bias is applied to the gas distribution showerhead to ignite the N₂O gas into a plasma. The RF bias is about 600 W at a frequency of about 13.56 MHz. The power density for the N₂O plasma treatment is between about 0.10 W/cm² and about 0.35 W/cm².

Now that the N₂O plasma treatment is completed, deposition of the passivation layers can begin. In order to prepare the processing chamber for deposition of the first passivation layer, the RF bias to the showerhead is turned off and the chamber pressure is reduced to about 800 mTorr over a period of about 15 seconds in step 4. During step 4, the N₂O gas continues to flow into the chamber at about 5658 sccm and SiH₄ gas begins to flow into the chamber at a rate of about 48 sccm. The substrate to gas distribution showerhead remains at about 500 mils during step 4. Step 5 beings by maintaining the flow of SiH₄ and N₂O gas at about 48 sccm and about 5658 sccm respectively while the substrate is spaced from the gas distribution showerhead by about 500 mils. The chamber pressure of about 800 mTorr is maintained for about 158 seconds while about 715 W RF power is applied to the gas distribution showerhead at about 13.56 MHz. At the completion of step 5, the first passivation layer of silicon oxide has been deposited.

In step 6, the processing chamber is prepared for deposition of the second passivation layer. In step 6, the processing chamber pressure is increased to about 1200 mTorr over a period of about 15 seconds while the substrate to gas distribution showerhead spacing is increased to about 800 mils. During step 6, the RF bias to the showerhead is turned off as is the flow of N₂O gas. The flow of SiH₄ gas, on the other hand, is increased to about 60 sccm, and N₂ gas and NH₃ gas are introduced at flow rates of about 3500 sccm and about 600 sccm respectively. After step 6, step 7 begins by applying RF bias to the showerhead at about 600 W and a frequency of about 13.56 MHz for about 97 seconds. The flow rate of SiH₄, N₂ and NH₃ remains at about 60 sccm, about 3500 sccm and about 600 sccm respectively. At the completion of step 7, the second passivation layer of silicon nitride has been deposited over the first passivation layer. During each of steps 1-7, the processing chamber is maintained at a temperature of between about 200 degrees Celsius and about 250 degrees Celsius. Thus, the N₂O plasma treatment, the first passivation layer deposition and the second passivation layer deposition all occur in-situ the same chamber.

FIGS. 10A-10C show the effects of N₂O plasma treatment on the TFT. FIG. 10A shows treatment shows a gradient change in the chemical states of IGZO—SiO₂ interface. While FIG. 10B shows a sharp change in chemical states at the IGZO—SiO₂ interface due to the lack of N₂O plasma treatment. The spectra used to create the x-ray photoelectron spectroscopy depth profiles for FIGS. 10A-10B were taken at every 50 Angstrom in depth. As shown in FIG. 10C, no TFT characteristic IV curve can be observed without N₂O plasma treatment.

FIG. 11 is a cross sectional view of a PECVD apparatus that may be utilized to produce the thin film transistors described here. The apparatus includes a chamber 1100 in which one or more films may be deposited onto a substrate 1120. The chamber 1100 generally includes walls 1102, a bottom 1104 and a showerhead 1106 which define a process volume. A substrate support 1118 is disposed within the process volume. The process volume is accessed through a slit valve opening 1108 such that the substrate 1120 may be transferred in and out of the chamber 1100. The substrate support 1118 may be coupled to an actuator 1116 to raise and lower the substrate support 1118. Lift pins 1122 are moveably disposed through the substrate support 1118 to move a substrate to and from the substrate receiving surface. The substrate support 1118 may also include heating and/or cooling elements 1124 to maintain the substrate support 1118 at a desired temperature. The substrate support 1118 may also include RF return straps 1126 to provide an RF return path at the periphery of the substrate support 1118.

The showerhead 1106 is coupled to a backing plate 1112 by a fastening mechanism 1150. The showerhead 1106 may be coupled to the backing plate 1112 by one or more fastening mechanisms 1150 to help prevent sag and/or control the straightness/curvature of the showerhead 1106.

A gas source 1132 is coupled to the backing plate 1112 to provide gas through gas passages in the showerhead 1106 to a processing area between the showerhead 1106 and the substrate 1120. A vacuum pump 1110 is coupled to the chamber 1100 to control the process volume at a desired pressure. An RF source 1128 is coupled through a match network 1190 to the backing plate 1112 and/or to the showerhead 1106 to provide an RF current to the showerhead 1106. The RF current creates an electric field between the showerhead 1106 and the substrate support 1118 so that a plasma may be generated from the gases between the showerhead 1106 and the substrate support 1118.

A remote plasma source 1130, such as an inductively coupled remote plasma source 1130, may also be coupled between the gas source 1132 and the backing plate 1112. Between processing substrates, a cleaning gas may be provided to the remote plasma source 1130 so that a remote plasma is generated. The radicals from the remote plasma may be provided to chamber 1100 to clean chamber 1100 components. The cleaning gas may be further excited by the RF source 1128 provided to the showerhead 1106.

The showerhead 1106 may additionally be coupled to the backing plate 1112 by showerhead suspension 1134. In one embodiment, the showerhead suspension 1134 is a flexible metal skirt. The showerhead suspension 1134 may have a lip 1136 upon which the showerhead 1106 may rest. The backing plate 1112 may rest on an upper surface of a ledge 1114 coupled with the chamber walls 1102 to seal the chamber 1100.

By treating the active channel of an IGZO or zinc oxide TFT with an N₂O or O₂ plasma after defining the source and drain electrodes but before formation of passivation or etch stop layers, a consistent TFT may be produced with minimal risk of plasma damage.

While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow. 

1. A method of forming a thin film transistor, comprising: depositing an active layer over a substrate in a thin film transistor; and exposing the active layer to a N₂O or O₂ plasma.
 2. The method of claim 1, further comprising: forming an etch stop layer over the plasma treated active layer; and defining source and drain electrodes over the plasma treated active layer.
 3. The method of claim 1, further comprising: forming an active channel by defining source and drain electrodes over the plasma treated active layer to expose a portion of the plasma treated active layer; and depositing one or more passivation over the active channel.
 4. The method of claim 1, wherein the active layer comprises a material selected from the group consisting of zinc oxide, indium-gallium-zinc oxide, and combinations thereof.
 5. The method of claim 4, wherein the exposing the active layer to a N₂O or O₂ plasma occurs at a temperature of between about 150 degrees Celsius and about 270 degrees Celsius.
 6. The method of claim 5, wherein the N₂O or O₂ plasma exposure occurs at a power density of between about 0.083 W/cm² and about 1.0 W/cm².
 7. The method of claim 6, wherein the N₂O or O₂ plasma exposure occurs at a pressure of between about 0.8 Torr and about 2.5 Torr.
 8. The method of claim 7, wherein the N₂O or O₂ plasma exposure occurs while a substrate upon which the thin film transistor is formed is spaced between about 500 mils and about 1100 mils from an electrode.
 9. The method of claim 4, wherein exposing the active layer to a N₂O or O₂ plasma comprises exposing the active channel to N₂O plasma.
 10. The method of claim 9, wherein the exposing the active layer to a N₂O plasma occurs at a temperature of between about 150 degrees Celsius and about 270 degrees Celsius.
 11. The method of claim 10, wherein the N₂O plasma exposure occurs at a power density of between about 0.083 W/cm² and about 1.0 W/cm².
 12. The method of claim 11, wherein the N₂O plasma exposure occurs at a pressure of between about 0.8 Torr and about 1.2 Torr.
 13. The method of claim 12, wherein the N₂O plasma exposure occurs while a substrate upon which the thin film transistor is formed is spaced between about 500 mils and about 800 mils from an electrode.
 14. A method of forming a thin film transistor, comprising: forming a gate electrode over a substrate; depositing a gate dielectric layer over the gate electrode and the substrate; depositing an indium-gallium-zinc oxide active layer over the gate dielectric layer; depositing a conductive layer over the active layer; removing at least a portion of the conductive layer to form source and drain electrodes and to form an active channel by exposing a portion of the active layer; exposing the active channel to a N₂O or O₂ plasma; and depositing one or more passivation or etch stop layers over the N₂O or O₂ plasma treated active channel.
 15. The method of claim 14, wherein the exposing the active channel to a N₂O or O₂ plasma occurs at a temperature of between about 150 degrees Celsius and about 270 degrees Celsius.
 16. The method of claim 15, wherein the N₂O or O₂ plasma exposure occurs at a power density of between about 0.083 W/cm² and about 1.0 W/cm².
 17. The method of claim 16, wherein the N₂O or O₂ plasma exposure occurs at a pressure of between about 0.8 Torr and about 2.5 Torr.
 18. The method of claim 17, wherein the N₂O or O₂ plasma exposure occurs while the substrate is spaced between about 500 mils and about 1100 mils from an electrode.
 19. A method of forming a thin film transistor, comprising: forming a gate electrode over a substrate; depositing a gate dielectric layer over the gate electrode and the substrate; depositing a zinc oxide active layer over the gate dielectric layer; depositing a conductive layer over the active layer; removing at least a portion of the conductive layer to form source and drain electrodes and to form an active channel by exposing a portion of the active layer; exposing the active channel to a N₂O or O₂ plasma; and depositing one or more passivation or etch stop layers over the N₂O or O₂ plasma treated active channel.
 20. The method of claim 19, wherein the exposing the active channel to a N₂O or O₂ plasma occurs at a temperature of between about 150 degrees Celsius and about 270 degrees Celsius, wherein the N₂O or O₂ plasma exposure occurs at a power density of between about 0.083 W/cm² and about 1.0 W/cm², wherein the N₂O or O₂ plasma exposure occurs at a pressure of between about 0.8 Torr and about 2.5 Torr and wherein the substrate is spaced between about 500 mils and about 1100 mils from an electrode. 